Catalytic hydrogenation of olefins, hydrodesulfurization of organic sulfur compounds and/or selective removal of hydrogen sulfide from fluid streams

ABSTRACT

Hydrogen sulfide is removed from a fluid stream by contacting the fluid stream which contains hydrogen sulfide with an absorbing composition comprising zinc, titanium and at least one promoter selected from the group consisting of vanadium, chromium, manganese, iron, cobalt, nickel, molybdenum, rhenium, and compounds thereof. If organic sulfur compounds are present in the fluid stream, the absorbing composition acts as a hydrodesulfurization catalyst to convert the sulfur in the organic sulfur compounds to hydrogen sulfide which is subsequently removed from the fluid stream by the absorbing composition. If olefin contaminants are present in the fluid stream, the absorbing composition acts as hydrogenation catalyst to hydrogenate the olefin contaminants to paraffins.

This application is a division of application Ser. No. 190,004, filedSept. 23, 1980, now U.S. Pat. No. 4,313,820, which is acontinuation-in-part of application Ser. No. 125,438, filed Feb. 28,1980, now abandoned.

This invention relates to an improved process for removing sulfur fromfluid streams and/or hydrogenating olefins contained in the fluidstreams. In one aspect this invention relates to an improved process forselectively removing hydrogen sulfide from fluid streams. In anotheraspect this invention relates to an improved process forhydrodesulfurizing (HDS) organic sulfur compounds contained in a fluidstream to convert the sulfur in the organic sulfur compounds to hydrogensulfide and for removing the thus produced hydrogen sulfide, and anyother hydrogen sulfide present in the fluid stream, from the fluidstream. In still another aspect of this invention relates to a processfor hydrogenating olefins to paraffins to improve the odor of a fluidcontaining the olefins.

Removal of sulfur from fluid streams can be desirable or necessary for avariety of reasons. If the fluid stream is to be burned as a fuel,removal of sulfur from the fluid stream can be necessary to preventenvironmental pollution. If the fluid stream is to be processed, removalof the sulfur is often necessary to prevent poisoning ofsulfur-sensitive catalysts or to satisfy other process requirements.

A variety of methods are available to remove sulfur from a fluid streamif the sulfur is present as hydrogen sulfide. These methods includeusing alkaline reagents that unselectively absorb all acid gases. Othermethods include the use of selective solid adsorbents such as zinc oxideand bog iron ore. However, in general these solid adsorbents are notregenerable to their original form and must be discarded when they havebecome completely sulfided.

It is thus an object of this invention to provide an improved processfor selectively removing hydrogen sulfide from fluid streams. It is afurther object of this invention to provide an improved removal orabsorbing composition which possesses the property of being regenerableto the original absorbing composition state in the presence of oxygen.

If the sulfur is present in the fluid stream in the form of an organicsulfur compound, the organic sulfur compound may be hydrodesulfurized toconvert the sulfur in the organic sulfur compound to hydrogen sulfidewhich can be removed from the fluid stream by an absorbing composition.

It is thus another object of this invention to provide a process for notonly removing hydrogen sulfide from a fluid stream but alsohydrodesulfurizing organic sulfur compounds to convert the sulfur in theorganic sulfur compounds to hydrogen sulfide which can then beselectively removed from the fluid stream.

The presence of olefin contaminants in a fluid may result in a foul odorassociated with the fluid. Also, the olefin contaminants may be oxidizedto even more malodorous products when released into the air. This isparticularly the case in aerosol propellants. It is thus another objectof this invention to provide a process for hydrogenating olefincontaminants in a fluid and particularly in aerosol propellants.

In accordance with the present invention, an absorbing compositioncomprising zinc, titanium and a promoter is utilized to selectivelyremove hydrogen sulfide, if present, from a fluid stream. The promoteris at least one member selected from the group consisting of vanadium,chromium, manganese, iron, cobalt, nickel, molybdenum, rhenium andcompounds thereof. The absorbing composition can be formed by combiningzinc oxide and titanium dioxide by any of the methods known in the artto form zinc titanate. The promoter can then be added to the zinctitanate. Once the absorbing composition has been prepared, fluidstreams are contacted with the absorbing composition under suitableabsorbing conditions to substantially reduce the concentration ofhydrogen sulfide in the fluid stream.

The absorbing composition also acts as a hydrodesulfurization catalystif organic sulfur compounds are present in the fluid stream. Undersuitable hydrodesulfurization conditions the organic sulfur compoundsare converted to hydrogen sulfide in the presence of the absorbingcomposition which acts as a hydrodesulfurization catalyst. Afterconversion to hydrogen sulfide, the sulfur will be removed from thefluid stream by the absorbing composition.

The absorbing composition also acts as an olefin hydrogenation catalystif olefin contaminants are present in the fluid stream. Under suitableolefin hydrogenation conditions the olefin contaminants are hydrogenatedto paraffins in the presence of the absorbing composition which acts asan olefin hydrogenation catalyst. The paraffins do not have theundesirable odor and are not readily oxidized to malodorous productswhen released into the air.

It is believed that the hydrogen sulfide is being absorbed by theabsorbing composition and thus the term "absorption process" and"absorbing composition" are utilized for the sake of convenience.However, the exact chemical phenomenon occurring is not the inventivefeature of the process of the present invention and the use of the term"absorb" in any form is not intended to limit the present invention.

Hereinafter, the process of the present invention is referred to by aplurality of terms depending on the reactions occurring. Terms utilizedinclude selective absorption or absorption process, hydrodesulfurizationprocess, olefin hydrogenation process and combinations thereof. The term"absorbing composition" is utilized to refer to the promoted zinctitanate in general although the term "catalyst/absorbing composition"is also utilized in some cases where the promoted zinc titanate isacting as a hydrodesulfurization catalyst, as a hydrogenation catalystand/or as an absorbing composition.

The selective absorption process is preferably carried out in cyclescomprising an absorption period and a regeneration period for theabsorbing composition. The absorption period comprises contacting afluid stream containing hydrogen sulfide with the absorbing compositionto thereby selectively remove hydrogen sulfide from the fluid stream.The absorbing composition becomes sulfided during the absorption period.When the absorbing composition becomes sulfided to the point thatregeneration is desirable, preferably when it is substantiallycompletely sulfided, a gas containing molecular oxygen is passed incontact with the absorbing composition to regenerate the absorbingcomposition and convert the absorbed sulfur to an oxide.

The hydrodesulfurization/absorption process is also preferably carriedout in cycles comprising a reaction period and a regeneration period forthe catalyst. The reaction period comprises contacting a fluid streamcontaining organic sulfur compounds with thehydrodesulfurization/absorption composition to thereby convert thesulfur in organic sulfur compounds in the fluid stream to hydrogensulfide. The hydrodesulfurization/absorption composition becomessulfided during the reaction period. When the composition becomessubstantially completely sulfided, a gas containing molecular oxygen ispassed in contact with the hydrodesulfurization/absorption compositionto regenerate the composition and to convert the absorbed sulfur to anoxide.

Olefin hydrogenation may be combined with either a selective absorptionprocess or a hydrodesulfurization/absorption process. Olefinhydrogenation may also occur when sulfur is not present in the fluidstream being contacted with the promoted zinc titanate. In all of thesecases the process is still carried out in cycles comprising a reactionperiod and a regeneration period. It is, however, noted that, if sulfuris not present in the fluid stream, the length of the reaction period isdetermined by coke buildup on the catalyst.

If desired, at least one oxidation promoter selected from the groupconsisting of ruthenium, rhodium, palladium, silver, tungsten, iridium,platinum, and compounds thereof may also be present to promote theregeneration of the absorbing composition.

The chemical changes that are believed to occur in the absorbingcomposition during this cyclic process where sulfur is present aresummarized in the following equations:

    Zn.sub.2 TiO.sub.4 +2H.sub.2 S→2ZnS+TiO.sub.2 +2H.sub.2 O (I)

    ZnS+Oxygen→ZnO+SO.sub.x                             (II)

    2ZnO+TiO.sub.2 →Zn.sub.2 TiO.sub.4                  (III)

Other objects and advantages of the invention will be apparent from theforegoing description of the invention and the appended claims as wellas from the detailed description of the invention which follows.

Any suitable organic sulfur compound may be hydrodesulfurized inaccordance with the present invention. Suitable organic sulfur compoundsinclude sulfides, disulfides, mercaptans, carbonyl sulfides, thiophenes,benzothiophenes, dibenzothiophenes and mixtures of any two or morethereof.

The absorbing composition of the present invention may be utilized toremove hydrogen sulfide from any suitable fluid stream. The hydrogensulfide may be produced by the hydrodesulfurization of organic sulfurcompounds or may be originally present in the fluid stream as hydrogensulfide. Suitable fluid streams include light hydrocarbons such asmethane, ethane and natural gas, petroleum products and products fromextraction and/or liquefaction of coal and lignite, products from tarsands, products from shale oil, coal derived synthesis gas, gases suchas hydrogen and nitrogen, gaseous oxides of carbon, steam, and the inertgases such as helium and argon. Gases that adversely affect the removalof hydrogen sulfide and which should be absent from the fluid streamsbeing processed are oxidizing agents such as molecular oxygen, thehalogens, the oxides of nitrogen, and the like.

The absorbing composition of the present invention may be utilized toremove hydrogen sulfide from olefins such as ethylene. However, thisprocess should be carried out in the absence of free hydrogen to avoidhydrogenation. Olefin streams should not be hydrodesulfurized as thismay result in undesirable hydrogenation of at least a portion of theolefins to paraffins.

The absorbing composition of the present invention may be utilized tohydrogenate olefin contaminants in any suitable fluid stream. It isparticularly desirable to remove olefin contaminants from C₃ and C₄paraffins such as isobutane, n-butane and propane which are utilized asaerosol propellants. The present invention is particularly directed tohydrogenating light olefins such as ethylene, propylene, n-butenes,isobutene, n-pentenes and branched pentenes contained in aerosolpropellants.

The absorbing composition employed in the process of the presentinvention is a composition consisting essentially of zinc, titanium anda promoter. The promoter is at least one member selected from the groupconsisting of vanadium, chromium, manganese, iron, cobalt, nickel,molybdenum, rhenium, and compounds thereof. At least one oxidationpromoter selected from the group consisting of ruthenium, rhodium,palladium, silver, tungsten, iridium, platinum, and compounds thereof,may also be present in the absorbing composition. The zinc and titaniumare generally present in the absorbing composition as zinc titanate. Thepromoters may be present in the absorbing composition as oxides,sulfides or as the free element. A preferred combination of promoters iscobalt oxide plus molybdenum oxide where the cobalt:molybdenum atomicratio is in the range of 0.3:1 to about 0.8:1.

The zinc titanate base of the absorbing composition may be prepared byintimately mixing suitable portions of zinc oxide and titanium dioxide,preferably in a liquid such as water, and calcining the mixture in a gascontaining molecular oxygen at a temperature in the range of about 650°C. to about 1050° C., preferably in the range of about 675° C. to about975° C. A calcining temperature in the range of about 800° C. to about850° C. is most preferred because the surface area of the catalyst ismaximized in this temperature range thus producing a more activecatalyst. The titanium dioxide used in preparing the zinc titanatepreferably has extremely fine particle size to promote intimate mixingof the zinc oxide and titanium dioxide. This produces a rapid reactionof the zinc oxide and titanium dioxide which results in a more activecatalyst. Preferably the titanium dioxide has an average particle sizeof less than 100 millimicrons and more preferably less than 30millimicrons. Flame hydrolyzed titanium dioxide has extremely smallparticle size and is particularly preferred in preparing the catalyst.The atomic ratio of zinc to titanium can be any suitable ratio. Theatomic ratio of zinc to titanium will generally lie in the range ofabout 1:1 to about 3:1 and will preferably lie in the range of about1.8:1 to about 2.2:1 because the activity of the absorbing compositionis greatest for atomic ratios of zinc to titanium in this preferredrange. The term "zinc titanate" is used regardless of the atomic ratioof zinc to titanium.

The zinc titanate base of the absorbing composition may also be preparedby coprecipitation from aqueous solutions of a zinc compound and atitanium compound. The aqueous solutions are mixed together and thehydroxides are precipitated by the addition of ammonium hydroxide. Theprecipitate is then washed, dried and calcined as described in thepreceding paragraph. This method of preparation is less preferred thanthe mixing method because the zinc titanate prepared by thecoprecipitation method is softer than the zinc titanate prepared by themixing method.

The promoter, at least one member of which is selected from the groupconsisting of vanadium, chromium, manganese, iron, cobalt, nickel,molybdenum, rhenium, and compounds thereof, is generally present in theabsorbing composition in the oxide form. The oxidation promoter, atleast one member of which is selected from the group consisting ofruthenium, rhodium, palladium, silver, tungsten, iridium, platinum, andcompounds thereof will generally be present in the absorbing compositionas the free metal or the oxide form if utilized. The promoter orcombination of promoters can be added to the zinc titanate by any methodknown in the art. The promoter or combination of promoters can be addedto the zinc titanate as powdered oxide and dispersed by any method knownin the art such as rolling, shaking or stirring. The preferred method ofadding the promoter is by impregnating the preformed zinc titanate witha solution of a compound of the promoting element. After impregnation,the absorbing composition is preferably dried to remove solvent and isthen heated in air at a temperature in the range of about 500° to about650° C., preferably about 540° C., before being utilized for theabsorption process or hydrodesulfurization/absorption process. If morethan one promoter is to be used, the absorbing composition is preferablydried and calcined after each promoter addition.

The concentration of the promoter in the absorbing composition may beany suitable concentration. The concentration of vanadium, chromium,manganese, iron, cobalt, nickel, or molybdenum expressed as an element,if present, will generally be in the range of about 0.4 to 16 weightpercent based on the weight of the promoted absorbing composition. Acombination of these promoters may be utilized. However, the totalconcentration of the promoters, expressed as an element, should be inthe range of about 1 to about 28 weight percent based on the weight ofthe promoted absorbing composition. The concentration of rhenium,expressed as an element, will generally be in the range of about 0.05 toabout 2.5 weight percent based on the weight of the promoted absorbingcomposition. The rhenium may also be utilized in combination with thevanadium, chromium, manganese, iron, cobalt, nickel, and molybdenum butagain the total concentration of the promoters, expressed as an element,should not exceed 28 weight percent based on the weight of the promotedabsorbing composition. The concentration of ruthenium, rhodium,palladium, silver, iridium or platinum, expressed as an element, ifpresent, will generally be in the range of about 0.05 to about 2.5weight percent based on the weight of the promoted absorbingcomposition. The concentration of tungsten, expressed as an element, ifpresent, will generally be in the range of about 0.4 to about 16 weightpercent based on the weight of the promoted absorbing composition. Theoxidation promoters, if utilized, are always utilized in combinationwith the promoters, at least one member of which is selected from thegroup consisting of vanadium, chromium, manganese, iron, cobalt, nickel,molybdenum, rhenium, and compounds thereof. Again, the totalconcentration of the promoters, including the oxidation promoters,should not exceed 28 weight percent based on the weight of the promotedabsorbing composition.

Either the elemental form of the promoters or any suitable compound ofthe promoters may be used to form the absorbing composition. Suitablecompounds of the promoting elements that can be applied to zinc titanateby solution impregnation include the nitrates, sulfates, acetates andthe like of chromium, manganese, iron, cobalt, nickel, and silver;ammonium salts of vanadates, molybdates, tungstates, rhenates andperrhenates; and nitrates, chlorides, or hexachloro ammonium salts ofruthenium, rhodium, palladium; and dihydrogen hexachloroplatinate.

The processes of the present invention can be carried out by means ofany apparatus whereby there is achieved an alternate contact of theabsorbing composition with the fluid stream and thereafter of theabsorbing composition with a fluid containing molecular oxygen utilizedto regenerate the absorbing composition. The process is in no waylimited to the use of a particular apparatus. The process of thisinvention can be carried out using a fixed absorbing composition bed,fluidized absorbing composition bed or moving absorbing composition bed.Presently preferred is a fixed absorbing composition bed.

In order to avoid any casual mixing of the fluid stream which containsorganic sulfur compounds, olefin contaminants and/or hydrogen sulfidewith the oxygen-containing fluid utilized in the regeneration step,provision is preferably made for terminating the flow of the fluidstream to the reactor and subsequently injecting an inert purging fluidsuch as nitrogen, carbon dioxide or steam. Any suitable purge time canbe utilized but the purge should be continued until all hydrocarbonand/or hydrogen are removed. Any suitable flow rate of the purge fluidmay be utilized. Presently preferred is a purge fluid flow rate in therange of about 800 GHSV to about 1200 GHSV.

Any suitable temperature for the processes of the present invention maybe utilized. For both absorption and olefin hydrogenation thetemperature will generally be in the range of about 149° C. to about538° C. and will more preferably be in the range of about 204° C. toabout 399° C. For hydrodesulfurization the temperature will generally bein the range of about 205° C. to about 538° C. and will more preferablybe in the range of about 260° C. to about 427° C.

Any suitable temperature may be utilized to regenerate the absorbingcomposition from its sulfided form back to the original absorbingcomposition form or to simply burn off carbon if only olefinhydrogenation is occurring. The temperature will generally be in therange of about 370° C. to about 815° C. A temperature of at least 540°C. is preferred to effect the conversion within a reasonable time.

Any suitable pressure for the processes of the present invention can beutilized. For hydrodesulfurization the pressure will range of from aboutatmospheric to about 1,000 psig. This pressure is the sum of the partialpressure of the fluid stream plus the partial pressure of the addedhydrogen. Preferably, the pressure will be in the range of from about 15psig to about 200 psig with about 80 psig being particularly preferredfor economy of operation as a cyclic process. The low pressure at whichthe hydrodesulfurization can be accomplished is a particularlyadvantageous feature of the present invention.

For olefin hydrogenation the pressure will range from about 100 psig toabout 1000 psig with a pressure in the range of about 100 psig to about500 psig being preferred. Again the pressure is the sum of the partialpressure of the fluid stream plus the partial pressure of the addedhydrogen.

The pressure of the fluid stream being treated is not believed to havean important effect on the absorption process of the present invention.The pressure will be in the range of from about atmospheric to at least2,000 psig during the treatment.

Any suitable quantity of hydrogen can be added to acomplish thehydrodesulfurization and/or olefin hydrogenation. The quantity ofhydrogen used to contact the fluid stream containing the organic sulfurcompounds being hydrodesulfurized will generally be in the range ofabout 100 to about 10,000 SCF/bbl and will more preferably be in therange of about 250 to about 3,000 SCF/bbl. For olefin hydrogenation, thehydrogen concentration should be at least sufficient to hydrogenate allolefins, i.e., mole percent hydrogen added should equal mole percentolefins. Preferably, the mole percent hydrogen will be 2-3 times themole percent of olefins. The presence of additional hydrogen is notrequired for the absorption process.

Any suitable residence time for the fluid stream in the presence of theabsorbing composition of the present invention can be utilized. Wherethe fluid stream is a liquid, the residence time in terms of the volumesof liquid per volume of absorbing composition per hour will generally bein the range of about 0.1 to about 50 and will more preferably be in therange of about 1 to about 20. Where the fluid stream is a gaseousstream, the residence time expressed as volumes of gas at standardtemperature and pressure per volume of absorbing composition per hourwill generally be in the range of about 10 to about 10,000 and will morepreferably be in the range of about 250 to about 2500.

The absorbing composition of the present invention continues to beeffective for converting organic sulfur compounds to hydrogen sulfide orhydrogenating olefin contaminants even when completely sulfided.However, when the absorbing composition is completely sulfided it willno longer combine with the hydrogen sulfide in the manner set forth inequation (I). When this condition occurs, hydrogen sulfide will begin toappear in the effluent flowing from the reaction and this will be anindication that the absorbing composition should preferably beregenerated. The time required for the absorbing composition to becomecompletely sulfided will generally be a function of the concentration ofsulfur in the feedstock and feed rate employed.

When the absorbing composition becomes substantially completelysulfided, the absorbing composition is typically regenerated byterminating the flow of feed to the reactor and purging with an inertfluid such as nitrogen to remove any combustibles. A freeoxygen-containing fluid is then introduced to oxidize the zinc sulfidein accordance with equation (II). Also at the temperature at which theoxidation of the zinc sulfide is effected, the zinc oxide thus producedrecombines with the titanium dioxide to resynthesize the original zinctitanate in accordance with equation (III).

If only olefin hydrogenation is occurring, the regeneration step may beutilized to remove coke from the promoted zinc titanate when thecatalyst becomes fouled. If absorption is occurring, the promoted zinctitanate will generally become completely sulfided long before theformation of coke becomes a problem. Thus, sulfiding of the catalystgenerally determines the length of the reaction period if absorption isoccurring.

If absorption is occurring, the amount of oxygen, from any source,supplied during the regeneration step will generally be in an amountsufficient to at least substantially remove sulfur from the absorbingcomposition. The regeneration step is conducted at generally aboutatmospheric pressure. The temperature for the regeneration step ispreferably maintained in the range of about 370° to about 815° C. and ismore preferably maintained at about 540° C. in order to both oxidize thezinc sulfide and convert the zinc oxide and titaium dioxide to zinctitanate within a reasonable time. If absorption is not occurring, theamount of oxygen, from any source, supplied during the regeneration stepwill be at least the amount sufficient to remove substantially allcarbonaceous materials from the promoted zinc titanate.

Examination of absorbing composition from various stages of the cyclicprocess confirms the suppositions made by observing reaction productsfrom process studies. Zinc titanate promoted with about 18 weightpercent of cobalt and molybdenum oxides shows an X-ray diffractionpattern of only the Zn₂ TiO₄. When completely sulfided, the X-raydiffraction pattern becomes zinc sulfide (both wurtzite and sphalerite)and titanium dioxide (anatase only). After regeneration with air, theabsorbing composition again has an X-ray diffraction pattern identicalwith that of the original material except for the occasional observationof traces of zinc molybdate. Presumably, both the cobalt and molybdenumfollow the zinc in being oxides or sulfides. It has been noted thatrepetitive operation through these cycles causes a significant increasein the surface area of the zinc titanate absorbing composition. Thesurface area of the zinc titanate absorbing composition is higher in thesulfided form than in the oxidized form. Reformation of zinc titanate inthis process occurs at a temperature significantly lower than thatrequired to synthesize the material when starting with the pure oxides.

The following examples are presented in further illustration of theinvention.

EXAMPLE 1

Zinc titanate having an atomic ratio of Zn:Ti=2.0:1 was prepared bymixing 162.8 g (2 moles) of Mallinckrodt zinc oxide with 79.9 g (onemole) of Cab-O-Ti titanium dioxide (flame hydrolyzed) in 1200 mL ofwater in a blender for 10 minutes. The resulting slurry was oven driedat 105° C. and then calcined in air for 3 hours at 816° C. Aftercooling, the thus calcined material was crushed and screened. Portionsof the screened zinc titanate having the size set forth in Table I weremodified by the addition of various promoters to produce absorbingcompositions A-G.

The general method for preparing each absorbing composition was asfollows. A weighed portion of zinc titanate, prepared as previouslydescribed, having a known pore volume was covered with a solution(generally aqueous) of known concentration of the promoting element.After standing one hour at 25° C., excess solution was removed bydecanting or filtering and the wet catalyst was dried, with occasionalstirring, in an oven, on a hot plate, or under a heat lamp. The driedcatalyst was calcined in air in a muffle furnace for 3-4 hours at 538°C., cooled in a desiccator, and reweighed. The quantity of promoteradded by this procedure was considered to be calculable from the volumeof promoter solution contained in the pores of the zinc titanate.Occasionally, this quantity was checked by observing the gain in weightof the absorbing composition made as described, but this gain was notconsidered to provide a definitive value of concentration. To add morethan one promoter, the entire procedure described here was repeated foreach impregnation.

The concentration of the promoter in the solution used to impregnate thezinc titanate to a desired level was calculated from the formula##EQU1## where n=number of atoms of promoter element per molecule ofcompound. To illustrate, to prepare an absorbing composition containing8.0 weight percent molybdenum on zinc titanate that has 0.8 mL/g porevolume, using ammonium heptomolybdate tetrahydrate as the source ofmolybdenum. ##EQU2##

The composition, size, and surface area of absorbing compositions A-Gare summarized in Table I. In every case zinc titanate comprised theunreported portion of the absorbing composition.

                  TABLE I                                                         ______________________________________                                                                             Sur-                                                                          face                                     Absorbing                  Size,     Area                                     Compositions                                                                           Promoters, Wt. %  U.S. Sieve                                                                              m.sup.2 /g                               ______________________________________                                        A        6.4 CoO, 11.3 MoO.sub.3, 0.1 Pt                                                                 - 8 + 14  3.0                                      B        0.2 CoO, 0.65 MoO.sub.3                                                                         -16 + 40  5.8                                      C        2.8 CoO, 5.0 MoO.sub.3                                                                          -16 + 40  5.9                                      D        4.0 NiO, 13.0 MoO.sub.3                                                                         -16 + 40  4.3                                      E        7.6 NiO, 24 WO.sub.3                                                                            -16 + 40  5.8                                      F        2.6 Re.sub.2 O.sub.7                                                                            -16 + 40  6.0                                      G        13.0 MoO.sub.3    -16 + 40  5.1                                      ______________________________________                                    

The promoters were added as aqueous solutions of the following salts.Cobalt as Co(NO₃)₂.6H₂ O, molybdenum as (NH₄)₆ Mo₇ O₂₄.4H₂ O, platinumas H₂ PtCl₆.6H₂ O, nickel as Ni(NO₃)₂.6H₂ O, tungsten as (NH₄)₂ W₄O₁₃.8H₂ O, and rhenium as NH₄ ReO₄.

Absorbing composition A from Table I was used in a cyclic manner forhydrodesulfurization (HDS). A complete process cycle consisted of:

(1) Hydrotreating 2.75 weight percent thiophene in cyclohexane (1.0 wt.% organic sulfur) at 160 psig pressure for 120 minutes between 370°-427°C. using 3.0 LHSV and adding about 0.5 mole hydrogen per mole of liquidfeed,

(2) Terminating the flow of the feed,

(3) Purging with nitrogen for 30 minutes while temperature is increasedto about 566° C.,

(4) Regenerating the thus purged absorbing composition A with air for120 minutes at 566° C.,

(5) Terminating the flow of the air,

(6) Purging with nitrogen for 30 minutes while temperature cools toabout 370° C.,

(7) Purging with hydrogen for 30 minutes at 370°-427° C. and thenintroducing feed per step (1). Steps 3, 4, 6 and 7 were all made atpressures between 0--30 psig.

Results obtained through 95 cycles of operation are summarized in TableII.

                  TABLE II                                                        ______________________________________                                                              HDS wt. %                                                                     of sulfur                                                                     originally Cyclohexane                                  Cycle No.                                                                              HDS Temp., °C.                                                                      present    Loss, %                                      ______________________________________                                        10       432          99         3                                            27       381          84         0                                            72       377          94         0                                            87       387          82         0                                            88-95 comp.                                                                            388          >90        0                                            ______________________________________                                    

During each 120 minute process cycle, 10.5 weight percent of theoriginal sulfur required to completely sulfide the absorbing compositionwas introduced into the reactor. (It is believed that cobalt andmolybdenum, in addition to the zinc, become sulfided.) Table II showsthat hydrodesulfurization activity was sustained during the 95 cyclesthat absorbing composition A was used.

Absorbing compositions B through G were used inhydrodesulfurization/absorption runs that demonstrate thehydrodesulfurization/absorption process. Table III, which describes thefeedstock and summarizes run conditions, shows that all of theseabsorbing compositions were active to hydrodesulfurize organic sulfurcompounds, and frequently the absorbing composition activity improvedwith use. Table III also shows that after use the absorbing compositioncontained approximately the stoichiometric concentration of sulfur. (Forreference unpromoted Zn₂ TiO₄ in which the zinc has been completelysulfided contains 23.34 weight percent sulfur.) After regeneration theconcentration of sulfur was substantially reduced. X-ray diffractionanalysis indicates that the sulfur was retained in the sulfide form, notas sulfate. X-ray diffraction showed also that the predominantcrystalline components of used absorbing compositions were zinc sulfideand titanium dioxide. After regeneration, zinc titanate was theprincipal crystalline component. Table III also shows the surface areaof the sulfided catalyst to be substantially larger than that of theregenerated form of the absorbing compositions.

                                      TABLE III                                   __________________________________________________________________________               HDS wt %                                                                      of sulfur                  Absorbing Composition                   Absorbing                                                                            No. of                                                                            originally                                                                          Absorbing Composition After HDS                                                                    After Regen.sup.(3)                     Compositions                                                                         Regen.                                                                            present.sup.(1)                                                                     Wt. % S                                                                            Wt. % C                                                                            SA, m.sup.2 /g                                                                     XRD.sup.(2)                                                                         Wt. % S                                                                            SA, m.sup.2 /g                                                                     XRD.sup.(2)                   __________________________________________________________________________    B      Fresh                                                                             85.3  20.3 0.56 22.5 ZnS,TiO.sub.2,                                                                      0.80 5.3  ZT,trZnO,                            1   84.0  22.4 0.60 19.5 trZT  ND   ND   trZnS                                2   88.0  23.6 0.82 ND         1.0  5.6                                C      Fresh                                                                             92.5  21.8 0.46 13.3 ZnS,TiO.sub.2,                                                                      1.28 6.6  ZT                                   1   98.9  27.8 0.83 21.1 trZT  2.0  8.5                                       2   98.9  20.6 1.01 20.1       3.1  5.9                                D      Fresh                                                                             93.9  25.1 0.36 ND   ZnS,TiO.sub.2,                                                                      4.45 8.2  ZT,ZnS,trZnO,                        1   98.7  22.6 0.83 17.6 Ni.sub.3 S.sub.2 MoS.sub.2                                                          3.93 7.0  trTiO.sub.2,trZnMoO.sub.4     E      Fresh                                                                             94.7  15.2 0.39 ND   ZnS,TiO.sub.2                                                                       8.34 ND   ZT,ZnS,ZnO                           1   90.9  15.9 0.29  8.2 ZT,ZnWO.sub.4                                                                            7.2  TiO.sub.2,ZnWO.sub.4          F      Fresh                                                                             80.5  20.8 0.36 14.9 ZnS,TiO.sub.2                                                                       4.86 9.6  ZT,trTiO.sub.2,                      1   92.3  22.0 0.55 25.0       ND   ND                                 G      Fresh                                                                             87.5  22.6 0.47 ND   ZnS,TiO.sub.2                                                                       1.37 ND   ZT,ZnMoO.sub.4                __________________________________________________________________________     .sup.(1) Tested at 399° C., 500 psig, 1.0 LHSV using feedstock fro     70% straight run distillate plus 30% 105-388° C. light cycle oil       (0.75 wt. % organic S in blend); 9.5 moles hydrogen per mole liquid feed;     runs 24-60 hr. duration.                                                      .sup.(2) ZnS: wurtzite plus sphalerite; TiO.sub.2 : anatase only; ZT: zin     titanate; tr: trace                                                           .sup.(3) Absorbing composition was regenerated for 2 hours at 538°     C. in air in a muffle furnace.                                           

EXAMPLE 2

Direct comparisons of hydrodesulfurization activity were made betweenzinc oxide and zinc titanate where both were unpromoted, where both werepromoted with molybdenum oxide only, and where both were promoted withcobalt molybdate. All runs were made over a range of temperatures at 1.0LHSV, 500 psig reactor pressure with 5000 SCF hydrogen per barrel offeed. The feedstock was a 104°-388° C. boiling range distillate thatcontained 0.73 wt. % organic sulfur. Girdler G-720 zinc oxide (acommercial desulfurization catalyst) and zinc titanate synthesized asdescribed in Example 1 were used to make these runs. Promoters wereadded to the zinc oxide and zinc titanate using the method described inExample 1. In all cases the absorbing compositions were-20+40 mesh U.S.sieve fraction. All catalysts were regenerated in air for two hours at538° C.

Results from runs with unpromoted zinc oxide and zinc titanate aresummarized in Table IV.

                  TABLE IV                                                        ______________________________________                                                     ZnO        Zn.sub.2 TiO.sub.4                                                 Fresh  Regen.  Fresh    Regen.                                   ______________________________________                                        Absorbing Composition                                                         Surface area, m.sup.2 /g                                                                     10.5     10.5     7.6    7.6                                   HDS, wt % of sulfur                                                           originally present:                                                            650° F.                                                                              40.0     22.7    28.0   33.3                                    700           49.3     29.3    46.7   43.3                                    750           45.3     42.7    54.7   60.0                                    775           53.3     52.0    66.7   70.7                                   Absorbing Composition                                                         Inspection:                                                                    Carbon, wt. % 0.34     0.28    0.30   0.57                                    Sulfur, wt. %                                                                  After HDS    15.0     18.8    13.3   17.6                                     After regen. 11.9     11.7     7.1   10.8                                   XRD analysis after HDS:                                                                      ZnO              Zn.sub.2 TiO.sub.4                                           ZnS              ZnS                                                                           TiO.sub.2                                                                     (anatase)                                     XRD analysis after regen.                                                                    ZnO              Zn.sub.2 TiO.sub.4                                           ZnS              ZnS                                                          ZnSO.sub.4       TiO.sub.2                                                                     (anatase)                                     ______________________________________                                    

Although both absorbing compositions showed significanthydrodesulfurization activity when fresh, zinc oxide was inferior at alltemperatures after regeneration. In contrast zinc titanate tended toimprove after regeneration. Neither absorbing composition regeneratedwell as indicated by their sulfur content.

Results from runs using zinc oxide and zinc titanate promoted only withmolybdenum trioxide are summarized in Table V.

                  TABLE V                                                         ______________________________________                                                     12.75 wt %                                                                              13.2 wt %                                                           MoO.sub.3 /ZnO                                                                          MoO.sub.3 /Zn.sub.2 TiO.sub.4                                       Fresh Regen.  Fresh     Regen.                                   ______________________________________                                        Absorbing Composition                                                         Surface area, m.sup.2 /g                                                                     6.5     N.D.    5.3     7.6                                    HDS, wt % of sulfur                                                           originally present:                                                            650° F.                                                                              75.3    34.7    63.9    54.7                                    700           88.1    48.0    84.7    81.3                                    750           95.9    65.3    97.6    96.0                                    775           98.1    72.0    96.1    97.1                                   Absorbing Composition                                                         Inspection:                                                                    Carbon, wt. % 0.35    0.27    0.72    0.55                                    Sulfur, wt. %                                                                  After HDS    12.0    28.5    20.3    21.3                                     After regen. 10.8    16.5    0.73    not                                                                           regen.                                 XRD analysis after HDS:                                                                      ZnS             ZnS                                                                           TiO.sub.2                                                                     (trace                                                                        rutile)                                        XRD analysis after regen:                                                                    ZnS             Zn.sub.2 TiO.sub.4                                                            ZnO-trace                                                                     ZnMoO.sub.4 -                                                                 trace                                          ______________________________________                                    

Unused zinc oxide promoted with molybdenum trioxide is seen to beexcellent for hydrodesulfurization. After regeneration itshydrodesulfurization activity has decreased markedly. In contrast, zinctitanate promoted with molybdenum oxide, while possibly less active whenunused, is seen to be appreciably more active after regeneration. Sulfuranalyses showed that the promoted zinc titanate gave up a much largerfraction of its sulfur than the promoted zinc oxide did whenregenerated. In addition the promoted zinc oxide contained enoughinactive zinc sulfate (ZnSO₄) to be seen by X-ray diffraction analysis.

Results from runs using oxide and zinc titanate promoted with cobaltmolybdate are summarized in Table VI.

                  TABLE VI                                                        ______________________________________                                                   Absorbing Composition                                                         4.0 wt % CoO--                                                                            3.4 wt % CoO--                                                    12.3 wt %   14.7 wt %                                                         MoO.sub.3 /ZnO                                                                            MoO.sub.3 /Zn.sub.2 TiO.sub.4                                     Fresh   Regen.  Fresh     Regen.                                   ______________________________________                                        Surface area, m.sup.2 /g                                                                   N.D.**    N.D.    8.6     N.D.                                   HDS, wt % of sulfur                                                           originally present:                                                            650° F.                                                                            73.3      78.7    93.3    88.0                                    700         85.3      86.7    98.7    94.7                                    750         94.7      92.0    94.7    98.7                                    775         97.2      94.7    99.6    99.2*                                  Absorbing                                                                     Composition                                                                   Inspection:                                                                    Carbon, wt. %                                                                             0.30      0.30    0.65    0.58                                    Sulfur, wt. %                                                                  After HDS  16.8      29.0    24.8    24.2                                     After regen.                                                                             13.3      21.2    1.1     not                                                                           regen.                                 XRD analysis after                                                            HDS:         ZnS               ZnS                                                         ZnMoO.sub.4 -     TiO.sub.2                                                   trace             (anatase)                                      XRD analysis after                                                            regen.:      ZnS               ZnTiO.sub.4                                                 ZnO               ZnO-trace                                                   ZnMoO.sub.4       ZnMoO.sub.4 -                                               ZnSO.sub.4        trace                                          ______________________________________                                         *At 800° F.; not measured at 775° F.                            **Not determined but prepared by adding cobalt to the MoO.sub.3 /ZnO          preparation of Table V; S.A. = 6.5 m.sup.2 /g before this impregnation.  

Zinc oxide and zinc titanate are both effective hydrodesulfurizationabsorbing compositions when promoted with cobalt molybdate. However, thepromoted zinc titanate was shown to be superior when fresh and alsoafter regeneration when compared with the promoted zinc oxide. Again,the sulfur analyses showed that zinc titanate gave up a much largerfraction of sulfur than the zinc oxide did upon being regenerated.

EXAMPLE 3

Zinc titanate having an atomic ratio of Zn:Ti=1.8:1 was prepared bymixing 73.2 g (0.9 moles) of Mallinckrodt zinc oxide with 40.0 g (0.5moles) of Cab-O-Ti titanium dioxide (flame hydrolyzed) in 600 cc ofwater in a blender for 10 minutes. The resulting slurry was oven driedat 105° C. and then calcined in air for 4 hours at 815° C. Aftercooling, the thus calcined material was crushed and screened. A -10+40mesh fraction of the screened zinc titanate was retained to prepareabsorbing compositions H and I.

Absorbing composition H was prepared by soaking 32.2 g of the zinctitanate in an excess of solution prepared by dissolving 17.42 g of(NH₄)₆ Mo₇ O₂₄.4 H₂ O and 19.02 g of Co(NO₃)₂.6 H₂ O in water containingsufficient ammonia to completely dissolve the cobalt compound anddiluting to 150 mL. Excess solution was removed by filtration. Theresulting residue was dried and calcined in air at 538° C. for one hour.The resulting solid (absorbing composition H) contained, by chemicalanalysis, 2.80 weight percent CoO and 7.95 weight percent MoO₃, and hada surface area of 5.9 m² /g.

Absorbing composition I was prepared by soaking 55 g of the zinctitanate in an excess of solution containing 17.4 g of (NH₄)₆ Mo₇ O₂₄.4H₂ O/100 mL. Excess solution was removed by filtration. The resultingresidue was dried and calcined in air at 538° C. for one hour. Aftercooling the resulting solid was soaked in a solution that contained 20.9g of Co(NO₃)₂.6 H₂ /100 mL. Again excess solution was removed byfiltration. The resulting residue was dried and calcined in air at 538°C. for one hour. The resulting solid absorbing composition I contained,by chemical analysis, 5.21 weight percent CoO and 13.35 weight percentMoO₃, and had a surface area of 6.5 m² /g.

Prior to being used as a hydrogen sulfide absorbent, absorbingcomposition H was used as a catalyst to hydrodesulfurize a petroleumfraction. Absorbing composition H was subjected to three periods ofsulfiding followed by oxidative regeneration. Hydrodesulfurization runswere at 500 psig using temperatures between 315°-427° C.--conditionsequivalent to those desired for H₂ S adsorption. Regeneration was withair for two hours at 538° C. The absorption process is illustrated bythe sulfur content of absorbing composition H determined by chemicalanalysis of a small, representative sample from each phase of theoperation as is set forth in Table VII.

                  TABLE VII                                                       ______________________________________                                        Original sample  0.00 wt. % sulfur                                            After 1st HDS run                                                                              21.8 wt. % sulfur                                            After 1st regeneration                                                                         1.28 wt. % sulfur                                            After 2nd HDS run                                                                              27.8 wt. % sulfur                                            After 2nd regeneration                                                                         3.87 wt. % sulfur                                            After 3rd HDS run                                                                              20.6 wt. % sulfur                                            After 3rd regeneration                                                                         3.09 wt. % sulfur                                            ______________________________________                                    

Elemental analysis, weight changes, and X-ray diffraction data ofabsorbing composition H after each hydrodesulfurization period and eachregeneration period showed no evidence of formation of inactive ZnSO₄.

Following the three hydrodesulfurization periods and the threeregeneration periods set forth in Table VII, absorbing composition Hsupplemented with 3.75 g of fresh absorbing composition H to replace theportion of absorbing composition H which had been expended for chemicalanalyses to obtain the data set forth in Table VII, was used in a run toremove hydrogen sulfide from a gas mixture prepared to simulate naturalgas. The gas mixture was a blend synthesized to contain nominally fivemole percent each of hydrogen sulfide and carbon dioxide in methane. Thegas mixture was passed through a stainless steel tube reactor mountedvertically in an electrically heated tube furnace at a space rate of 366hr.⁻¹ for 4.5 hours at 373° C. and atmospheric pressure. The stainlesssteel tube contained absorbing composition H. Analyses of effluent gasmade during the run using Drager tubes (calibrated colorimetricdetectors from National Drager, Inc., Pittsburgh, Pa., and availablethrough laboratory and safety equipment suppliers) were consistentlynegative, indicating that less than 0.04 ppm hydrogen sulfide remainedin the gas. Analyses in triplicate of the feed sample and the effluentproduct by gas-liquid chromatography (GLC) for carbon dioxide showed6.49 and 6.74 mole percent, respectively. These concentrations show thatessentially none of the carbon dioxide was removed from the methanewhile no detectable amount of hydrogen sulfide was found in theeffluent. At the conclusion of the run about 41 percent of the zinc inabsorbing composition H had been sulfided.

Prior to being utilized as a hydrogen sulfide adsorbent, absorbingcomposition I was used as a catalyst to hydrodesulfurize a petroleumfraction. Absorbing composition I was subjected to two periods ofhydrodesulfurization with a regeneration period between the twohydrodesulfurization periods. Hydrodesulfurization runs were at 500 psigusing temperatures between 315° and 427° C. Regeneration was with airfor two hours at 538° C. The absorption process is illustrated by thesulfur content of absorbing composition I determined by chemicalanalysis of a small, representative sample from each phase of theoperation as set forth in Table VIII.

                  TABLE VIII                                                      ______________________________________                                        Original sample  0.00 wt. % sulfur                                            After 1st HDS run                                                                              21.0 wt. % sulfur                                            After 1st regeneration                                                                          8.0 wt. % sulfur                                            After 2nd HDS run                                                                              23.2 wt. % sulfur                                            ______________________________________                                    

24.26 g of absorbing composition I remained after the analysis wasperformed after the second hydrodesulfurization run set forth in TableVIII. The remaining portion of absorbing composition I was regeneratedin air at 538° C. for two hours and then used, without being analyzedfor sulfur, in a run to remove hydrogen sulfide from the effluent of anoperating hydrodesulfurization process. The hydrodesulfurizationeffluent contained, by analysis, 0.49 mole percent hydrogen sulfide. Theconcentration of the other components of the hydrodesulfurizationeffluent was not determined although the hydrodesulfurization effluentwas known to be principally hydrogen with small amounts of hydrocarbons.Absorbing composition I was contained in a stainless steel tube reactorwhich was mounted vertically in a tube furnace. The hydrodesulfurizationeffluent was passed over absorbing composition I at a space rate of 1200hours⁻¹ for 5.5 hours at a temperature of 400° C. and atmosphericpressure. Analysis of the hydrodesulfurization effluent, after thehydrodesulfurization effluent had been contacted with absorbingcomposition I, with Drager tubes was negative which indicates that thehydrogen sulfide concentration was less than 0.04 ppm.

The temperature of absorbing composition I was reduced to 204° C. andthe hydrodesulfurization effluent was passed over absorbing compositionI in the stainless steel reactor at a space rate of 1200 hour⁻¹, for 4hours at atmospheric pressure. At the lower temperature of 204° C.,about 5 ppm hydrogen sulfide remained in the hydrodesulfurizationeffluent after the hydrodesulfurization effluent had been contacted withabsorbing composition I.

EXAMPLE 4

A catalyst having a composition nearly identical to that of absorbingcomposition H, in Example 3, was used to purify isobutane that was to beused as an aerosol propellant. The catalyst contained 2.6 wt. % CoO, 8.3wt. % MoO₃, had 9.8 m² /g surface area and 1.12 g/mL bulk density.Thirty mL of -20+40 mesh catalyst, loaded into a tubular reactor, wasplaced in a vertical, electrically heated, temperature controlledfurnace. Isobutane at 17.5 LHSV plus hydrogen at 215 SCF/bbl passeddownflow through the reactor at 300° C. and 1.34 MPa. The isobutaneinitially contained 2 parts per million total sulfur and from 20 to 150parts per million olefins. After treatment as described, it containedless than five parts per million olefins as measured by GLC, and had nosulfur or unpleasant odor.

Reasonable variations and modifications are possible within the scope ofthe disclosure and the appended claims to the invention.

That which is claimed is:
 1. A process for removing hydrogen sulfidefrom a fluid stream comprising the step of contacting said fluid streamunder suitable absorbing conditions with an incompletely sulfidedabsorbing composition comprising zinc titanate and at least one promoterselected from the group consisting of vanadium, chromium, manganese,iron, cobalt, nickel, molybdenum, rhenium, and compounds thereof,wherein the concentration by weight of said at least one promoter insaid absorbing composition is less than the total concentration byweight of said zinc titanate in said absorbing composition.
 2. A processin accordance with claim 1 wherein said fluid stream contains an olefincontaminant which is hydrogenated when said fluid stream is contactedwith said catalyst/absorbing composition.
 3. A process in accordancewith claim 2 wherein said fluid stream is an aerosol propellant selectedfrom the group consisting of isobutane, n-butane, propane and mixturesof any two or more thereof and said olefin contaminant is selected fromthe group consisting of ethylene, propylene, n-butenes, isobutene,n-pentenes and branched pentenes.
 4. A process in accordance with claim1 wherein said zinc titanate is prepared by calcining a mixture of zincoxide and titanium dioxide in the presence of molecular oxygen at atemperature in the range of about 650° C. to about 1050° C.
 5. A processin accordance with claim 4 wherein the atomic ratio of zinc to titaniumin said absorbing composition is in the range of about 1:1 to about 3:1.6. A process in accordance with claim 4 wherein the atomic ratio of zincto titanium in said absorbing composition is in the range of about 1.8:1to about 2.2:1.
 7. A process in accordance with claim 4 wherein saidabsorbing composition has been calcined in the presence of molecularoxygen at a temperature in the range of about 500° C. to about 650° C.after said at least one promoter has been added to said zinc titanate.8. A process in accordance with claim 7 wherein the concentration ofvanadium, chromium, manganese, iron, cobalt, nickel, or molybdenum asindividual promoters, if present, expressed as an element, is in therange of about 0.4 to about 16 weight percent based on the weight ofsaid absorbing composition and the concentration of rhenium as anindividual promoter, if present, expressed as an element, is in therange of about 0.05 to about 2.5 weight percent based on the weight ofsaid absorbing composition.
 9. A process in accordance with claim 8wherein the total concentration of any combination of the group fromwhich said at least one promoter is selected, expressed as an element,is in the range of about 1 to about 28 weight percent based on theweight of said absorbing composition.
 10. A process in accordance withclaim 1 wherein said at least one promoter is a combination of cobaltand molybdenum.
 11. A process in accordance with claim 10 wherein thecobalt:molybdenum atomic ratio in said absorbing composition is in therange of about 0.3:1 to about 0.8:1.
 12. A process in accordance withclaim 1 wherein said absorbing composition additionally comprises atleast one oxidation promoter selected from the group consisting ofruthenium, rhodium, palladium, silver, tungsten, iridium, platinum, andcompounds thereof.
 13. A process in accordance with claim 12 wherein theconcentration of ruthenium, rhodium, palladium, silver, iridium orplatinum as individual oxidation promoters, expressed as an element, ifpresent, is in the range of about 0.05 to about 2.5 weight percent basedon the weight of said absorbing composition and the concentration oftungsten as an individual promoter, expressed as an element, if present,is in the range of about 0.4 to about 16 weight percent based on theweight of said absorbing composition.
 14. A process in accordance withclaim 13 wherein the total concentration of any combination of said atleast one promoter and said at least one oxidation promoter, expressedas an element, is in the range of about 1 to about 28 weight percentbased on the weight of said absorbing composition.
 15. A process inaccordance with claim 1 wherein said suitable absorbing conditionscomprise a temperature in the range of about 149° C. to about 538° C., atotal system pressure in the range of about atmospheric to about 2000psig and a residence time for said fluid stream in the presence of saidabsorbing composition in the range of about 0.1 to about 50 liquidvolumes of said fluid stream per volume of said absorbing compositionper hour.
 16. A process in accordance with claim 1 wherein said suitableabsorbing conditions comprise a temperature in the range of about 204°C. to about 399° C., a total system pressure in the range of about 15psig to about 200 psig and a residence time for said fluid stream in thepresence of said absorbing composition in the range of about 1 to about5 liquid volumes of said fluid stream per volume of said absorbingcomposition per hour.
 17. A process in accordance with claim 2 whereinsaid suitable absorbing conditions comprise a temperature in the rangeof about 149° C. to about 538° C., a total system pressure in the rangeof about 100 psig to about 1000 psig, a hydrogen concentrationsufficient to hydrogenate all of said olefin contaminant and a residencetime for said fluid stream in the presence of said absorbing compositionin the range of about 0.1 to about 50 liquid volumes of said fluidstream per volume of said absorbing composition per hour.
 18. A processin accordance with claim 2 wherein said suitable absorbing conditionscomprise a temperature in the range of about 204° C. to about 399° C., atotal system pressure in the range of about 100 psig to about 500 psig,a mole percent hydrogen concentration in the range of about 2 to about 3times the mole percent of said olefin contaminants in said fluid streamand a residence time for said fluid stream in the presence of saidabsorbing composition in the range of about 1 to about 20 liquid volumesof said fluid stream per volume of said absorbing composition per hour.19. A process in accordance with claim 1 wherein said absorbingcomposition is sulfided during said process.
 20. A process in accordancewith claim 19 additionally comprising the steps of:discontinuing theflow of said fluid stream over said absorbing composition; andcontacting said absorbing composition, after the flow of said fluidstream is discontinued, with a molecular oxygen-containing fluid undersuitable regeneration conditions to thereby regenerate said absorbingcomposition.
 21. A process in accordance with claim 20 wherein saidsuitable regeneration conditions comprise a feed rate of said molecularoxygen-containing fluid suitable to supply sufficient oxygen to removesubstantially all of the sulfur from said absorbing composition, atemperature in the range of about 370° to about 815° C., and a pressurein the range of about atmospheric to about 1000 psig.
 22. A process inaccordance with claim 21 wherein sulfur is removed as an oxide duringsaid regeneration period.
 23. A process in accordance with claim 20additionally comprising the step of purging said absorbing compositionwith an inert fluid after the step of terminating the flow of said fluidstream and before the step of regenerating said absorbing composition.24. A process in accordance with claim 20 additionally comprising thesteps of:terminating the flow of said oxygen-containing fluid over saidabsorbing composition after said absorbing composition is substantiallyregenerated; purging said absorbing composition with an inert fluidafter the flow of said oxygen-containing fluid is terminated;terminating the flow of said inert fluid over said absorbing compositionafter said oxygen-containing fluid is substantially purged from saidabsorbing composition; and recontacting said absorbing composition withsaid fluid stream after the flow of said inert fluid is terminated. 25.A process for removing hydrogen sulfide from a fluid stream which doesnot contain hydrocarbons which are subject to dehydrogenation, reformingor hydrocracking comprising the step of contacting said fluid streamunder suitable absorbing conditions with an incompletely sulfidedabsorbing composition comprising zinc titanate.
 26. A process inaccordance with claim 25 wherein said zinc titanate is prepared bycalcining a mixture of zinc oxide and titanium dioxide in the presenceof molecular oxygen at a temperature in the range of about 650° C. toabout 1050° C.
 27. A process in accordance with claim 26 wherein theatomic ratio of zinc to titanium in said absorbing composition is in therange of about 1:1 to about 3:1.
 28. A process in accordance with claim26 wherein the atomic ratio of zinc to titanium in said absorbingcomposition is in the range of about 1.8:1 to about 2.2:1.
 29. A processin accordance with claim 25 wherein said suitable absorbing conditionscomprise a temperature in the range of about 149° C. to about 538° C., atotal system pressure in the range of about atmospheric to about 2000psig and a residence time for said fluid stream in the presence of saidabsorbing composition in the range of about 0.1 to about 50 liquidvolumes of said fluid stream per volume of said absorbing compositionper hour.
 30. A process in accordance with claim 25 wherein saidsuitable absorbing conditions comprise a temperature in the range ofabout 204° C. to about 399° C., a total system pressure in the range ofabout 15 psig to about 200 psig and a residence time for said fluidstream in the presence of said absorbing composition in the range ofabout 1 to about 5 liquid volumes of said fluid stream per volume ofsaid absorbing composition per hour.
 31. A process in accordance withclaim 25 wherein said absorbing composition is sulfided during saidprocess.
 32. A process in accordance with claim 31 additionallycomprising the steps of:discontinuing the flow of said fluid stream oversaid absorbing composition; and contacting said absorbing composition,after the flow of said fluid stream is discontinued, with a molecularoxygen-containing fluid under suitable regeneration conditions tothereby regenerate said absorbing composition.
 33. A process inaccordance with claim 32 wherein said suitable regeneration conditionscomprise a feed rate of said molecular oxygen-containing fluid suitableto supply sufficient oxygen to remove substantially all of the sulfurfrom said absorbing composition, a temperature in the range of about370° C. to about 815° C., and a pressure in the range of aboutatmospheric to about 1000 psig.
 34. A process in accordance with claim32 wherein sulfur is removed as an oxide during said regenerationperiod.
 35. A process in accordance with claim 32 additionallycomprising the step of purging said absorbing composition with an inertfluid after the step of terminating the flow of said fluid stream andbefore the step of regenerating said absorbing composition.
 36. Aprocess in accordance with claim 32 additionally comprising the stepsof:terminating the flow of said oxygen-containing fluid over saidabsorbing composition after said absorbing composition is substantiallyregenerated; purging said absorbing composition with an inert fluidafter the flow of said oxygen-containing fluid is terminated;terminating the flow of said inert fluid over said absorbing compositionafter said oxygen-containing fluid is substantially purged from saidabsorbing composition; and recontacting said absorbing composition withsaid fluid stream after the flow of said inert fluid is terminated.